In situ synchrotron x-ray diffraction (XRD) measurements of single-walled carbon nanotube (SWNT) and C60-Peapod samples under high pressure up to 13 GPa and at high temperature were carried out. Anisotropical shrinkages of their bundle 2-dimensional (2D) lattices were observed. It was found that the lattices recover original forms reversibly by releasing pressure. It was also found that phase transformations occur by raising temperature at the highest pressure. The high-pressure and high-temperature (HPHT) treated samples were examined by XRD, TEM, and Raman measurements.
Article
先進ファイバー工学研究教育拠点研究成果報告書 10: 34-35(2004)
信州大学繊維学部
2004-03-31
jpn
research report
VoR
http://hdl.handle.net/10091/13618
https://soar-ir.repo.nii.ac.jp/records/14569
AA1200368X
先進ファイバー工学研究教育拠点研究成果報告書
10
34
35
https://soar-ir.repo.nii.ac.jp/record/14569/files/AFSTT10-107.pdf
application/pdf
1.0 MB
2015-09-28