 author = {Pham,  Van Duc and Kobayashi,  Junya and Sugimoto,  Koh-ichi},
 issue = {11},
 journal = {TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN},
 month = {},
 note = {The effects of Cr, Mo and Ni additions on the microstructure and stretch-flangeability of 0.2%C-1.5%Si-1.5%Mn-0.05%Nb, in mass%, TRIPaided martensitic sheet steel produced by isothermal transformation process at a temperature below martensite-finish temperatures were investigated to develop the 3rd-generation sheet steel for automobile requiring high hardenability. When 0.5% or 1.0% Cr was added to the base steel, the combination of tensile strength of 1.5 GPa and hole-expanding ratio of 40% was attained. On the other hand, the Cr-Mo or Cr-MoNi addition hardly influenced the stretch-flangeability and stretch-formability, although it increased the yield and tensile strengths, comparing to the base steel. The good balance of Cr-bearing steel was mainly caused by suitable combination of (1) volume fraction and (2) interparticle path of finely dispersed martensite-austenite complex phase (M-A phase), which suppressed a void initiation at the matrix/M-A phase interface on hole-punching and void coalescence or crack extension on hole-expanding., Article, TETSU TO HAGANE-JOURNAL OF THE IRON AND STEEL INSTITUTE OF JAPAN. 99(11):659-668 (2013)},
 pages = {659--668},
 title = {TRIP型マルテンサイト鋼板の伸びフランジ性に及ぼす合金元素添加の影響},
 volume = {99},
 year = {2013}
}