@techreport{oai:soar-ir.repo.nii.ac.jp:00014513,
 author = {大越,  豊 and 後藤,  康夫 and 奈倉,  正宣 and 浦川,  宏},
 month = {Mar},
 note = {Fiber structure development in the poly (ethylene terephthalate) fiber drawing process was investigated by on-line measurement of wide-angle and small-angle x-ray scattering employing both a high-luminance x-ray source and a carbon dioxide laser-heated-drawing system. Intensity profile of transmitted x-ray confirmed the location of the neck-drawing point. Obtained diffraction images had a time-resolution of several milliseconds， which still leaves a great capacity for improvement. Crystal diffraction appeared in the wide-angle x-ray images almost instantaneously about 20 ms after necking, whereas a four-point SAXS pattern appeared immediately after necking. with the elapse of time after necking, the four-point scattering pattern changed to a merridional two-point shape., Article, 先進ファイバー工学研究教育拠点研究成果報告書 11: 113-114(2005)},
 title = {15-5-3 : レーザー加熱延伸による繊維構造形成過程の解析},
 year = {2005}
}